PC LUX9130T-NAT SABIC INNOVATIVE NANSHA

162
  • Unit Price:US$ 6,162 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant
  • Application Areas:Plastic bagLighting applications
  • Color:--
  • Grade:Halogen-free flame retardant grade

Technical Data Sheet Compare

thermal performanceTest ConditionTest MethodTest Result
Heat Deflection Temperature0.45 MPa, 未退火, 3.20 mmASTM D648131 °C
Heat Deflection Temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距8ISO 75-2/Be131 °C
Heat Deflection Temperature1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Heat Deflection Temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距8ISO 75-2/Ae120 °C
vicat--ASTM D15259137 °C
vicat--ISO 306/B120139 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8317.1E-5 cm/cm/°C
Linear coefficient of thermal expansion流动 : 23 到 80°CISO 11359-27.4E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8317.1E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-28.0E-5 cm/cm/°C
RTI ElecUL 746115 °C
RTI ImpUL 746115 °C
optical performance Test ConditionTest MethodTest Result
transmissivity1000 µm内部方法> 90.5 %
transmissivity2000 µm内部方法> 90.0 %
transmissivity3000 µm内部方法> 89.5 %
transmissivity6000 µmASTM D1003> 88.0 %
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.40 mmUL 94V-2
UL flame retardant rating1.5 mmUL 94V-0
UL flame retardant rating6.0 mmUL 945VA
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.5 mmIEC 60695-2-13850 °C
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CASTM D4812无断裂
Suspended wall beam without notch impact strength23°CASTM D4812无断裂
Suspended wall beam without notch impact strength-30°C7ISO 180/1U130 kJ/m²
Suspended wall beam without notch impact strength23°C7ISO 180/1U130 kJ/m²
Dart impact23°C, Total EnergyASTM D376355.0 J
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123818 g/10 min
Melt volume flow rate300°C/1.2 kgISO 113317.0 cm3/10min
shrinkage rate流动 : 3.20 mm内部方法0.45 - 0.65 %
shrinkage rate横向流动 : 3.20 mm内部方法0.50 - 0.70 %
Water absorption rate饱和, 23°CISO 620.10 %
Water absorption rate平衡, 23°C, 50% RHISO 620.010 %
Electrical performanceTest ConditionTest MethodTest Result
dielectric constant1.10 GHzASTM ES7-832.81
Dissipation Factor1.10 GHzASTM ES7-835.8E-3
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel265 to 290 °C
Temperature in the middle of the barrel275 to 300 °C
Temperature at the front of the material cylinder290 to 310 °C
Spray nozzle temperature280 to 305 °C
Processing (melt) temperature290 to 310 °C
mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6382370 Mpa
Tensile modulus--ISO 527-2/12400 Mpa
tensile strength屈服3ASTM D63864.0 Mpa
tensile strength屈服ISO 527-2/5064.0 Mpa
tensile strength断裂3ASTM D63859.0 Mpa
tensile strength断裂ISO 527-2/5050.0 Mpa
elongation屈服3ASTM D6386.0 %
elongation屈服ISO 527-2/506.0 %
elongation断裂3ASTM D63872 %
elongation断裂ISO 527-2/5052 %
flexural modulus50.0 mm 跨距4ASTM D7902300 Mpa
flexural modulus--5ISO 1782410 Mpa
bending strength屈服, 50.0 mm 跨距ASTM D79098.0 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.