PBT Cristin® SK605 DUPONT USA
238
- Unit Price:US$ 3,695 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:97MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% by weight ratio)｜30% filler by weight｜Good strength｜Good hardness (glass fiber reinforced
- Application Areas:Automotive Applications｜Electronic and electrical components｜Structural components｜Industrial applications｜Automotive Applications
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45Mpa,未退火 | ASTM D648 | 220 ℃ |
| 1.8Mpa,未退火 | ASTM D648 | 205 ℃ | |
| Linear coefficient of thermal expansion | 平行流动方向，73 to 130°F (23 to 55℃) | ASTM E831 | 0.000030 cm/cm/℃ |
| 垂直流动方向，73 to 130°F (23 to 55℃) | ASTM E831 | 0.000090 cm/cm/℃ | |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| 1.50 mm | UL 94 | HB | |
| 3.00 mm | UL 94 | HB | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 205 °C | |
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 224 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 41 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | refraction，F值 | ISO 6452 | 99 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Emissions of Organic Compounds | VDA277 | 140 µgC/g |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 19 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 10 kJ/m² |
| -30°C | ISO 179/1eA | 11 kJ/m² | |
| 23°C | ISO 179/1eA | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 75 kJ/m² |
| -30°C | ISO 179/1eU | 75 kJ/m² | |
| 23°C | ISO 179/1eU | 70 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 10 kJ/m² |
| -30°C | ISO 180/1A | 10 kJ/m² | |
| 23°C | ISO 180/1A | 11 kJ/m² | |
| Suspended wall beam without notch impact strength | -40°C | ISO 180/1U | 55 kJ/m² |
| -30°C | ISO 180/1U | 55 kJ/m² | |
| 23°C | ISO 180/1U | 60 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.53 | |
| melt mass-flow rate | ISO 1133 | 10 g/10min | |
| density | ISO 1183 | 1.53 g/cm³ | |
| MediumDensity | 1.36 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.35 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % | |
| viscosity number | ISO 307 | 100 cm³/g | |
| ThermalConductivityofMelt | 0.28 W/m/K | ||
| SpecificHeatCapacity of Melt | 1730 J/kg/°C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 38 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| 1MHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC 60250 | 7.5E-04 |
| 1MHz | IEC 60250 | 0.018 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -40℃ | ASTM D256 | 1120 J/m |
| 23℃ | ASTM D256 | 998 J/m | |
| compressive strength | 5 mm/min, 3.20 mm, 23 ℃ | ASTM D695 | 202 MPa |
| tensile strength | 23℃ | ASTM D638 | 140 MPa |
| Tensile modulus | 23℃ | ASTM D638 | 10000 MPa |
| flexural modulus | 23℃ | ASTM D790 | 8970 MPa |
| Elongation at break | 23℃ | ASTM D638 | 2.6 % |
| Impact strength of cantilever beam gap | ASTM D256 | 101 J/m | |
| -40℃ | ASTM D256 | 101 J/m | |
| 23℃ | ASTM D256 | 112 J/m | |
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 140 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.7 % |
| Tensile creep modulus | 1hr | ISO 899-1 | 9000 Mpa |
| 1000hr | ISO 899-1 | 6600 Mpa | |
| flexural modulus | ISO 178 | 9000 Mpa | |
| bending strength | ISO 178 | 200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.