Material Properties:High mobility｜High rigidity｜lubrication｜Filler: Glass fiber reinforced material｜60% filler by weight
Application Areas:Electronic and Electrical Applications｜Automotive components
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	23℃		122to125

thermal performance	Test Condition	Test Method	Test Result
1.8MPa, Not annealed		°C	139to288
1.8MPa, Not annealed	1.8MPa, Not annealed		°C	223to270
Linear coefficient of thermal expansion	MD	mm/mm/°C	30.5E-5到50.8E-5
0.45MPa, Not annealed		°C	253to262
0.45MPa, Not annealed	0.45MPa, Not annealed		°C	137to223
melting temperature		°C	220to265

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23℃	J/m	0.085to0.462
Impact strength of simply supported beam without notch	23℃	kJ/m²	7.892to21.357

Physical properties	Test Condition	Test Method	Test Result
Flow: 23 ℃	流动,23℃	mm/mm	25.4E-3-134.6E-3
Water absorption rate	23℃,24hr	%	0.15-0.53

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)		V
dielectric strength	23℃	V/mil	490to610
Surface Resistivity		ohms	1.0E+12-1.0E+14
volume resistivity	23℃	ohms·cm	1.0E+4-1.0E+16

mechanical properties	Test Condition	Test Method	Test Result
Yield, 23 ℃			27.03to260.0 MPa
Fracture, 23 ℃		%	1.7-2.7
	Fracture, 23 ℃			56.0to260.0 MPa
		Fracture, 23 ℃			26.0to260.0 MPa
		Fracture, 23 ℃	Fracture, 23 ℃		%	2.0-4.6
Yield, 23 ℃		%	1.5-5.0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.