Material Description
- Material Properties:heat-resisting｜Flame retardant｜enhance
- Application Areas:Household appliances｜Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | ISO 2039-2 | 71 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2E-05 cm/cm/°C |
| MD | ISO 11359-2 | 7E-06 cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 335 °C | |
| Vicat softening temperature | ISO 306/B50 | 195 °C | |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO 75-2/C | 216 °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 276 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 45 % | |
| UL flame retardant rating | UL 94 | V-0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.40 % |
| MD | ISO 294-4 | 0.10 % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.030 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation factor | 2.05GHz | Internal Method | 6E-03 |
| 1MHz | IEC 60250 | 0.025 | |
| 100Hz | IEC 60250 | 0.010 | |
| Relative permittivity | 2.05GHz | Internal Method | 4.23 |
| 1MHz | IEC 60250 | 3.30 | |
| 100Hz | IEC 60250 | 4.00 | |
| Dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the anti leakage trace index | IEC 60112 | V | |
| Arc resistance | Internal Method | 140 sec |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus | 23°C | ISO 178 | 13500 Mpa |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| Compressive modulus | ISO 604 | 14000 Mpa | |
| Fracture bending strain | ISO 178 | 2.2 % | |
| CompressiveStress | 1%Strain | ISO 604 | 93.0 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 15000 Mpa | |
| tensile strength | Break | ISO 527-2/1A/5 | 150 Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.6 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 31 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 43 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.