PC LEXAN™  EXL1112T WH4D290X SABIC INNOVATIVE SHANGHAI

228
  • Unit Price:US$ 3,928 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    36MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Processability｜Ductility｜copolymer｜High mobility
  • Application Areas:Electrical field｜Electronic field｜Fitness equipment｜Bottle cap
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity2540 μmASTM D100382.0 %
turbidity2540 μmASTM D10033.0 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA45 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376374.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94HB
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13850 °C
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span4ASTM D79094.0 Mpa
bending strength--5,6ISO 17889.0 Mpa
Bending modulus--5ISO 1782140 Mpa
Bending modulus50.0 mm Span4ASTM D7902240 Mpa
elongationBreakISO 527-2/50120 %
elongationBreak3ASTM D638120 %
elongationYieldISO 527-2/505.4 %
elongationYield3ASTM D6385.7 %
tensile strengthBreakISO 527-2/5056.0 Mpa
tensile strengthBreak3ASTM D63857.0 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
tensile strengthYield3ASTM D63858.0 Mpa
Tensile modulus--ISO 527-2/12340 Mpa
Tensile modulus--2ASTM D6382260 Mpa
injectionTest ConditionTest MethodTest Result
Exhaust hole depth0.025 to 0.076 mm
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648121 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af116 °C
Vicat softening temperature--ASTM D152510138 °C
Vicat softening temperature--ISO 306/B120139 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8317.5E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-27.5E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8317.6E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.6E-5 cm/cm/°C
RTI ElecUL 746130 °C
RTIUL 746130 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.090 %
Water absorption rateSaturation, 23°CISO 620.12 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.80 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113319.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123820 g/10 min
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityASTM D257> 1.0E+15 ohms
Volume resistivityASTM D257> 1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL -SaleISO 2039-289
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.