Material Description
- Material Properties:High mobility
- Application Areas:Lighting applications｜Automotive External Parts｜Architectural Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 16.0 cm3/10min | |
| ISO 1133 | 70.0 cm3/10min | ||
| Shrinkage rate | 内部方法 | 0.60 - 0.90 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | ISO 527-2/50 | 65.0 Mpa | |
| ISO 527-2/50 | 60.0 Mpa | ||
| Tensile strain | ISO 527-2/50 | 6.5 % | |
| ISO 527-2/50 | 80 % | ||
| Flexural modulus | ISO 178 | 2400 Mpa | |
| bending strength | ISO 178 | 100 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 12 kJ/m² | |
| ISO 179/1eA | 16 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 10 kJ/m² | |
| ISO 180/1A | 14 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 125 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 315 °C | ||
| Temperature in the middle of the barrel | 280 to 325 °C | ||
| Temperature at the front of the material cylinder | 290 to 335 °C | ||
| Spray nozzle temperature | 285 to 330 °C | ||
| Processing (melt) temperature | 290 to 335 °C | ||
| Temperature | 85 to 130 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 90 rpm | ||
| Exhaust hole depth | 0.025 to 0.080 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 144 °C | |
| ISO 75-2/Af | 132 °C | ||
| vicat | ISO 306/B50 | 150 °C | |
| ISO 306/B120 | 152 °C | ||
| Linear coefficient of thermal expansion | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| ISO 11359-2 | 7.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.