Material Description

Material Properties:Electrical performance
Application Areas:Casters｜Automotive Applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	4.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	V-2
Flammability level	Flammability level		UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--	ISO 527-2	3300	Mpa
	Tensile modulus	120°C	ISO 527-2	800	Mpa
		Tensile modulus	160°C	ISO 527-2	650	Mpa
			Tensile modulus	180°C	ISO 527-2	600	Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	500	Mpa
tensile strength	Yield	ISO 527-2	100	Mpa
	tensile strength	Yield, 120°C	ISO 527-2	50.0	Mpa
		tensile strength	Yield, 160°C	ISO 527-2	40.0	Mpa
			tensile strength	Yield, 180°C	ISO 527-2	35.0	Mpa
			tensile strength	tensile strength	Yield, 200°C	ISO 527-2	30.0	Mpa
Nominal tensile fracture strain	--	ISO 527-2	40	%
	Nominal tensile fracture strain	120°C	ISO 527-2	> 50	%
		Nominal tensile fracture strain	160°C	ISO 527-2	> 50	%
			Nominal tensile fracture strain	180°C	ISO 527-2	> 50	%
			Nominal tensile fracture strain	Nominal tensile fracture strain	200°C	ISO 527-2	> 50	%
Bending modulus	--	ISO 178	3000	Mpa
	Bending modulus	120°C	ISO 178	800	Mpa
	Bending modulus	Bending modulus	160°C	ISO 178	600	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	280	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	190	°C
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	8.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
RTI Elec	0.75 mm	UL 746	130	°C
Thermal Index - 5000 hr		IEC 60216	128	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.18	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	2.0	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	25	KV/mm
Relative permittivity	100 Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.60
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.