Material Properties:Processability｜Ductility｜copolymer｜High mobility
Application Areas:Electrical field｜Electronic field｜Fitness equipment｜Bottle cap
Color:--
Grade:Light diffusion level

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	2540 μm	ASTM D1003	82.0	%
turbidity	2540 μm	ASTM D1003	3.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	45	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	74.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.8 mm	IEC 60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2260	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2340	Mpa
tensile strength	Yield3	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	57.0	Mpa
		tensile strength	Break3	ASTM D638	57.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	56.0	Mpa
elongation	Yield3	ASTM D638	5.7	%
	elongation	Yield	ISO 527-2/50	5.4	%
		elongation	Break3	ASTM D638	120	%
		elongation	elongation	Break	ISO 527-2/50	120	%
Bending modulus	50.0 mm Span4	ASTM D790	2240	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2140	Mpa
bending strength	--5,6	ISO 178	89.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	94.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			270 to 295	°C
Temperature in the middle of the barrel			280 to 305	°C
Temperature at the front of the material cylinder			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Processing (melt) temperature			295 to 315	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	116	°C
Vicat softening temperature	--	ASTM D152510	138	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	139	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 95°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 95°C	ASTM E831	7.6E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5	cm/cm/°C
RTI Elec		UL 746	130	°C
RTI		UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	20	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	19.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80	%
Water absorption rate	Saturation, 23°C	ISO 62	0.12	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.090	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L -Sale	ISO 2039-2	89

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.