'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LEXAN™ 243R-111 SABIC INNOVATIVE SPAIN
65
- Unit Price:US$ 3,041 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Plastic bag
- Supply Quantity:24MT
- Delivery Terms:FOB
- Port of Loading :YANTIAN port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
Shenzhen City Yu Bang Plastic Materials Co., Ltd.
+86 1536********View
luoy********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Industrial applications｜Automotive sector｜Electrical appliances｜Lighting applications｜Plastic bag
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| turbidity | 2540μm | ASTM D1003 | 1.0 | % |
| transmissivity | 2540μm | ASTM D1003 | 88.0 | % |
| Refractive index | ASTM D542 | 1.586 | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 800 | J/m |
| ASTM D1822 | 546 | kJ/m² | ||
| Dart impact | 23°C | ASTM D3029 | 169 | J |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 3200 | J/m |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.75mm | UL 94 | V-2 | |
| 6.0mm | UL 94 | V-0 | ||
| Extreme Oxygen Index | ASTM D2863 | 25 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTM D1044 | 10.0 | mg |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 93.1 | Mpa |
| elongation | Break | ASTM D638 | 110 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2340 | Mpa |
| elongation | Yield | ASTM D638 | 7.0 | % |
| tensile strength | Break | ASTM D638 | 65.5 | Mpa |
| Yield | ASTM D638 | 62.1 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Str | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| thermal conductivity | ASTMC177 | 0.27 | W/m/K | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| Vicat softening temperature | ASTM D15255 | 154 | °C | |
| specific heat | ASTMC351 | 1260 | J/kg/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTM D648 | 132 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTM D648 | 138 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Outdoor applicability | UL 746C | f1 | ||
| Water absorption rate | Equilibrium,100°C | ASTM D570 | 0.58 | % |
| density | ASTM D792 | 1.20 | g/cm³ | |
| Specific volume | ASTM D792 | 0.830 | cm³/g | |
| density | ASTM D792 | 1.19 | g/cm³ | |
| Water absorption rate | Equilibrium,23°C | ASTM D570 | 0.35 | % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 | g/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 | % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257 | >1.0E+17 | ohms·cm | |
| Dielectric strength | 3.20mm,inAir | ASTM D149 | 15 | KV/mm |
| Dielectric constant | 50Hz | ASTM D150 | 3.17 | |
| 60Hz | ASTM D150 | 3.17 | ||
| 1MHz | ASTM D150 | 2.96 | ||
| Dissipation factor | 50Hz | ASTM D150 | 9E-04 | |
| 60Hz | ASTM D150 | 9E-04 | ||
| 1MHz | ASTM D150 | 0.010 | ||
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 2 | |
| High arc combustion index | HAI | UL 746 | PLC 1 | |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 2 | |
| Hot wire ignition | HWI | UL 746 | PLC 4 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ASTM D785 | 118 | |
| M-Sale | ASTM D785 | 70 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.