Material Properties:Low warpage｜Flame retardant｜Glass fiber reinforced
Application Areas:Electronic and electrical components｜Automotive Applications｜Industrial applications
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
characteristic			可加工性良好耐化学性良好
purpose			工业领域汽车领域的应用

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	HB
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	205 °C
	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	150 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,退火	ISO 75-2/A	180 °C
melting temperature		ISO 11357-3	225 °C

flammability	Test Condition	Test Method	Test Result
burning rate	1.00mm	ISO 3795	38 mm/min
UL flame retardant rating	1.5mm	UL 94,IEC60695-11-10,-20	HB

Supplementary Information	Test Condition	Test Method	Test Result
Odor		VDA270	3.50

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.35

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638/ISO 527	7000 kg/cm²(MPa)[Lb/in²]
flexural modulus		ASTM D790/ISO 178	6200 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	160 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2	7000 Mpa
tensile strength	断裂	ISO 527-2	108 Mpa
Tensile strain	断裂	ISO 527-2	2.5 %
flexural modulus		ISO 178	6200 Mpa
bending strength		ISO 178	160 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.