'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT VALOX™ 508-BK1066 SABIC INNOVATIVE SHANGHAI
16
- Unit Price:US$ 6,240 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Shanghai port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Shenzhen Jiuhe New Material Technology Co., Ltd.
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low warpage｜Glass fiber reinforced
- Application Areas:Laptop case｜Phone case｜Home appliance components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 640 | J/m |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 6.00 | J |
| 23°C, Total Energy | ASTM D3763 | 8.00 | J | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break | ASTM D638 | 110 | Mpa |
| Bending modulus | 50.0 mm Span | ASTM D790 | 6890 | Mpa |
| bending strength | Break, 50.0 mm Span | ASTM D790 | 189 | Mpa |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| Exhaust hole depth | 0.025 to 0.038 | mm | ||
| Screw speed | 50 to 80 | rpm | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Mold temperature | 65 to 90 | °C | ||
| Processing (melt) temperature | 250 to 265 | °C | ||
| Spray nozzle temperature | 245 to 260 | °C | ||
| Temperature at the front of the material cylinder | 250 to 265 | °C | ||
| Temperature in the middle of the barrel | 245 to 260 | °C | ||
| Temperature at the rear of the barrel | 240 to 255 | °C | ||
| Suggested injection volume | 40 to 80 | % | ||
| Suggested maximum moisture content | 0.020 | % | ||
| drying time | 3.0 to 4.0 | hr | ||
| drying temperature | 120 | °C | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 215 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 176 | °C | |
| Linear coefficient of thermal expansion | -40 to 40°C，Flow | ASTM E831 | 2.3E-5 | cm/cm/°C |
| 60 to 138°C，Flow | ASTM E831 | 1.6E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 125 | °C | |
| RTI Imp | UL 746 | 110 | °C | |
| RTI | UL 746 | 125 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.660 | cm³/g | |
| Shrinkage rate | Flow : 1.50 to 3.20 mm | Internal Method | 0.30 - 0.50 | % |
| Flow : 3.20 to 4.60 mm | Internal Method | 0.50 - 0.80 | % | |
| Across FlowFlow : 1.50 to 3.20 mm | Internal Method | 0.40 - 0.60 | % | |
| Across FlowFlow : 3.20 to 4.60 mm | Internal Method | 0.60 - 0.90 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 | % |
| Outdoor applicability | UL 746C | f2 | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257 | 5.9E+16 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 29 | KV/mm |
| Hot wire ignition | UL 746 | PLC 1 | ||
| High voltage arc tracing rate | UL 746 | PLC 2 | ||
| High arc combustion index | UL 746 | PLC 3 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 4 | ||
| Arc resistance | ASTM D495 | PLC 6 | ||
| Dissipation factor | 1 MHz | ASTM D150 | 0.020 | |
| 100 Hz | ASTM D150 | 1.4E-3 | ||
| Dielectric constant | 1 MHz | ASTM D150 | 3.60 | |
| 100 Hz | ASTM D150 | 3.60 | ||
| Dielectric strength | 3.20 mm, in Air | ASTM D149 | 24 | KV/mm |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 119 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.