PC PANLITE® L-1250Y BK TEIJIN SINGAPORE

239

Unit Price:US$ 2,461 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
16.9MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜Medium viscosity｜High mobility
Application Areas:Industrial components｜Household appliances｜Mechanical components｜Casters｜Labor protection equipment｜Nursing supplies
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.585
transmissivity	3000 μm	ASTM D1003	88.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	76 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.40 mm	UL 94	V-2
Burning wire flammability index	1.5 mm	IEC 60695-2-12	825 °C
Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	875 °C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2400 Mpa
tensile strength	Yield	ISO 527-2/50	61.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Nominal tensile fracture strain		ISO 527-2/50	> 50 %
Bending modulus		ISO 178	2350 Mpa
bending strength		ISO 178	93.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	142 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	129 °C
Vicat softening temperature		ISO 306/B50	149 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	7.0E-5 cm/cm/°C
RTI Elec	0.75 mm	UL 746	125 °C
RTI Imp	0.75 mm	UL 746	115 °C
RTI	0.75 mm	UL 746	125 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.20 g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	横向Flow : 4.00 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 4.00 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr, 23°C	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100 Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	3.00
Dissipation factor	100 Hz	IEC 60250	1.0E-3
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	9.0E-3
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.