PC TARFLON™ G-2530 IDEMITSU JAPAN

333

Unit Price:US$ 3,566 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜Flame retardant｜enhance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			一般级
remarks			特性：增强30%

machinability	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ASTM D-955	6.0
Shrinkage rate	Shrinkage rate	MD	ASTM D-955	1.5

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	23℃水中24h	ASTM D-570	0.11 %

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break		ASTM D638/ISO 527	3 %
bending strength		ASTM D790/ISO 178	170(1700) kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8530(8700) kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M92
tensile strength		ASTM D638/ISO 527	8100(83000) kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	15(16) kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO R-527 (ASTM D-638)	8100(83000) MPa(KG/cm
Bending modulus		ISO 178 (ASTM D-790)	8530(8700) MPa(KG/cm
Elongation at Break		ISO R-527 (ASTM D-638)	3 %
Impact strength of cantilever beam gap	4mm with notch 3.2mm with notch	ISO 180 (ASTM D-256)	15(16) KJ/m
Rockwell hardness		ISO 2039-2 (ASTM D-785)	M92
tensile strength	Break	ISO R-527 (ASTM D-638)	120(1200) MPa(KG/cm
bending strength		ISO 178 (ASTM D-790)	170(1700) Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306	150 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.3 mm/mm.℃
Vicat softening temperature		ASTM D1525/ISO R306	150 ℃（℉）
Combustibility (rate)		UL 94	V-2
Linear coefficient of thermal expansion		ASTM D-696	2.3
Combustibility	1.47mm厚	UL 94	V-2
Hot deformation temperature	1.80MPa,18.6kg/cm	ISO 75(ASTM D-648)	144 °C

Physical properties	Test Condition	Test Method	Test Result
Spiral flow length	3mm厚	出光法	23 CM
Water absorption rate		ASTM D570/ISO 62	0.11 %
Shrinkage rate		ASTM D955	1.5 %
density		ASTM D792/ISO 1183	1.42

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D-495	110 sec
Dielectric constant	60Hz	ASTM D-150	3.40
Dielectric strength	1.6mm厚	ASTM D-149	＜22 KV/mm
Dielectric constant	10	ASTM D-150	3.45
Inherent resistance of volume		ASTM D-257	＜10 Ω·cm
Induced positive connection	10	ASTM D-150	9×10
Induced positive connection	Induced positive connection	60Hz	ASTM D-150	8×10

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.