ABS POLYLAC® PA-756H TAIWAN CHIMEI

335

Unit Price:US$ 2,154 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:Household goods
Color:--
Grade:Injection grade

Material Certification

MSDS

RoHS

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.05 g/cm³
density	density		ISO 1183	1.05 g/cm³
melt mass-flow rate		ASTM D1238	8.0 g/10min
Melt volume flow rate		ISO 1133	80.0 cm3/10min
Shrinkage rate		ISO 294-4	0.40-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	115

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
elongation		ISO 527-2/50	35 %
Flexural modulus		ASTM D790	2210 Mpa
Flexural modulus	Flexural modulus		ISO 178	2200 Mpa
bending strength		ASTM D790	62.5 Mpa
bending strength	bending strength		ISO 178	65.0 Mpa
tensile strength		ASTM D638	39.1 Mpa
	tensile strength		ISO 527-2/50	44.0 Mpa
	tensile strength	tensile strength		ISO 527-2/50	33.0 Mpa
elongation		ASTM D638	10 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179	10 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	530 J/m
	Impact strength of cantilever beam gap		ASTM D256	480 J/m
		Impact strength of cantilever beam gap		ISO 180/1A	5.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	9.0 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	85.0 °C
	Heat distortion temperature		ISO 75-2/A	82.0 °C
		Heat distortion temperature		ASTM D648	95.0 °C
		Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	97.0 °C
vicat		ASTM D15257	105 °C
	vicat		ISO 306/A50	102 °C
	vicat	vicat		ISO 306/B50	95.0 °C
Linear coefficient of thermal expansion		ISO 11359-2	8.9E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.