LCP

LCP VECTRA® A950 CELANESE USA

264

Unit Price:US$ 17,379 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
102.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Corrosion resistance｜Thermal stability｜Weather resistance｜High rigidity｜high strength｜damping
Application Areas:Automotive sector｜Camera applications｜Electrical field｜Electronic field｜Optical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	250 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	270 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	53 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	158 Mpa
Bending modulus	23°C	ISO 178	9100 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	6600 Mpa
Tensile creep modulus	Tensile creep modulus	1 hr	ISO 899-1	9000 Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.1 %
tensile strength	Break	ISO 527-2/1A/5	200 Mpa
Tensile modulus		ISO 527-2/1A	11700 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.010 %
Hopper temperature			20 to 30 °C
Temperature at the rear of the barrel			270 to 280 °C
Temperature in the middle of the barrel			275 to 285 °C
Temperature at the front of the material cylinder			280 to 290 °C
Spray nozzle temperature			290 to 300 °C
Processing (melt) temperature			285 to 295 °C
Mold temperature			80 to 120 °C
Injection speed			快速
Back pressure			< 3.00 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow	ISO 11359-2	4.0E-6 cm/cm/°C
Melting temperature		ISO 11357-3	280 °C
Vicat softening temperature		ISO 306/B50	145 °C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	94.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	193 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	3.8E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.0E-3 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	6.0E-3 %
Shrinkage rate	Flow	ISO 294-4	0.0 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1 MHz	IEC 60250	3.00
Dissipation factor	100 Hz	IEC 60250	0.016
Relative permittivity	100 Hz	IEC 60250	3.20
Dielectric strength		IEC 60243-1	47 KV/mm
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Dissipation factor	1 MHz	IEC 60250	0.020
Compared to the anti leakage trace index	--	IEC 60112	V
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Solution B	IEC 60112	V
Surface resistivity		IEC 60093	1.0E+14 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP VECTRA® A950 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet