Material Description

Material Properties:Low temperature resistance｜Flame retardant｜transparent
Application Areas:household electrical appliances｜Electrical applications｜electrical equipment
Color:--
Grade:Cold resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
-30°C		ASTM D256	720 J/m
23°C		ASTM D256	820 J/m
-30°C		ISO 180/1A	55 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60 kJ/m²
23°C		ISO 180/1A	65 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	76.0 J

mechanical properties	Test Condition	Test Method	Test Result
yield		ASTM D638	5.8 %
crack		ISO 527-2/50	54.0 Mpa
crack	crack		ASTM D638	51.0 Mpa
yield		ISO 527-2/50	57.0 Mpa
yield	yield		ASTM D638	59.0 Mpa
--2		ASTM D638	2240 Mpa
Yield, 50.0mm span		ASTM D790	85.0 Mpa
--9		ISO 178	89.0 Mpa
--8		ISO 178	2150 Mpa
50.0mm span		ASTM D790	2220 Mpa
crack		ISO 527-2/50	110 %
crack	crack		ASTM D638	84 %
yield		ISO 527-2/50	5.4 %

thermal performance	Test Condition	Test Method	Test Result
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ISO 11359-2	8E-05 cm/cm/°C
Horizontal: -40 to 95 ° C	Across Flow, -40to95℃	ASTME831	8E-05 cm/cm/°C
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	6.7E-05 cm/cm/°C
Flow: -40 to 95 ° C	-40to95℃	ASTME831	6.7E-05 cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
1.8MPa, unannealed, 3.20mm		ASTM D648	122 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	116 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.090 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.12 %
Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80 %
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.40 cm3/10min
Shrinkage rate	MD1	Internal Method	0.40-0.80 %
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.40-0.80 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ FXE1414T-BK1A184T SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet