PA46 Stanyl® TW241F10 DSM HOLAND

335

Unit Price:US$ 11,315 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Lubricity
Application Areas:Electronic and electrical components｜Casters
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	290 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	290 °C
melting temperature		ISO 11357-3	295 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	4.0E-5 cm/cm/°C
RTI Elec	0.75 mm	UL 746	65.0 °C
Thermal Index - 5000 hr		IEC 60216	177 °C

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	16 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	14 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.62 g/cm³
shrinkage rate	横向流量	ISO 294-4	0.90 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	0.40 %
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	1.9 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	1.0E+14 ohms·cm
dielectric strength		IEC 60243-1	30 KV/mm
relative permittivity	100 Hz	IEC 60250	4.30
relative permittivity	relative permittivity	1 MHz	IEC 60250	4.00
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 2

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2	16000 Mpa
	Tensile modulus	120°C	ISO 527-2	8200 Mpa
		Tensile modulus	160°C	ISO 527-2	7400 Mpa
			Tensile modulus	180°C	ISO 527-2	7000 Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	6600 Mpa
tensile strength	断裂	ISO 527-2	250 Mpa
	tensile strength	断裂, 120°C	ISO 527-2	140 Mpa
		tensile strength	断裂, 160°C	ISO 527-2	120 Mpa
			tensile strength	断裂, 180°C	ISO 527-2	110 Mpa
			tensile strength	tensile strength	断裂, 200°C	ISO 527-2	100 Mpa
Tensile strain	断裂	ISO 527-2	2.7 %
	Tensile strain	断裂, 120°C	ISO 527-2	5.0 %
		Tensile strain	断裂, 160°C	ISO 527-2	5.0 %
			Tensile strain	断裂, 180°C	ISO 527-2	5.0 %
			Tensile strain	Tensile strain	断裂, 200°C	ISO 527-2	5.0 %
flexural modulus	--	ISO 178	14000 Mpa
	flexural modulus	120°C	ISO 178	7300 Mpa
	flexural modulus	flexural modulus	160°C	ISO 178	6500 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.