mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	15	%
tensile strength		ASTM D638/ISO 527	480	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	110
Bending modulus		ASTM D790/ISO 178	24000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	670	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	22	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	85	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.04
Shrinkage rate		ASTM D955	0.4—0.7	%
Water absorption rate		ASTM D570/ISO 62	0.3	%
melt mass-flow rate		ASTM D1238/ISO 1133	5.5	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	35	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.