PC LEXAN™ FXE1414 WH9D279 SABIC INNOVATIVE NANSHA
149
- Unit Price:US$ 3,415 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low temperature resistance｜transparent｜Flame retardant
- Application Areas:Electrical appliances｜Electronic field｜Electrical field｜Household appliances
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 139 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 124 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 128 °C | |
| vicat | ASTM D152510 | 145 °C | |
| -- | ISO 306/B50 | 145 °C | |
| -- | ISO 306/B120 | 146 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 139 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9 | ISO 75-2/Ae | 128 °C | |
| vicat | -- | ASTM D152510 | 145 °C |
| -- | ISO 306/B120 | 146 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| 23°C | ISO 179/1eA | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 60 kJ/m² |
| 23°C | ISO 180/1A | 70 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| 23°C | ISO 179/1eA | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 70.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.80 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.35 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| mold temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 55.5 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| 断裂 | ASTM D638 | 50.3 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 98 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2230 Mpa |
| ISO 178 | 2250 Mpa | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 92.4 Mpa | |
| Tensile modulus | --2 | ASTM D638 | 2020 Mpa |
| -- | ISO 527-2/1 | 2150 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 55.0 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| 断裂3 | ASTM D638 | 50.0 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂3 | ASTM D638 | 98 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2230 Mpa |
| --5 | ISO 178 | 2250 Mpa | |
| bending strength | --5,6 | ISO 178 | 85.0 Mpa |
| 屈服, 50.0 mm 跨距4 | ASTM D790 | 92.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.