LCP LAPEROS® E130i TAIWAN POLYPLASTICS
335
- Unit Price:US$ 8,584 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:141MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:heat-resisting｜Flame retardant｜enhance
- Application Areas:Household appliances｜Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40 % | |
| ISO 294-4 | 0.10 % | ||
| Water absorption rate | ISO 62 | 0.030 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 71 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 45 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 13500 Mpa | |
| bending strength | ISO 178 | 220 Mpa | |
| Compression Modulus | ISO 604 | 14000 Mpa | |
| Compressive Stress | ISO 604 | 93.0 Mpa | |
| Fracture bending strain | ISO 178 | 2.2 % | |
| Tensile modulus | ISO 527-2/1A/1 | 15000 Mpa | |
| tensile strength | ISO 527-2/1A/5 | 150 Mpa | |
| Tensile strain | ISO 527-2/1A/5 | 1.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 43 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 31 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| relative permittivity | IEC 60250 | 4.00 | |
| IEC 60250 | 3.30 | ||
| 内部方法 | 4.23 | ||
| Dissipation Factor | IEC 60250 | 0.010 | |
| IEC 60250 | 0.025 | ||
| 内部方法 | 6E-03 | ||
| arc resistance | 内部方法 | 140 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 276 °C | |
| ISO 75-2/C | 216 °C | ||
| vicat | ISO 306/B50 | 195 °C | |
| melting temperature | ISO 11357-3 | 335 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 7E-06 cm/cm/°C | |
| ISO 11359-2 | 2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.