PEEK

PEEK KetaSpire® PEEK KT-820SL45 SOLVAY USA

337

Unit Price:US$ 87,033 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
16MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Thrust washer｜Oil/Gas Supplies｜Application in the automotive field｜Bushing｜Engine parts
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	400°C,1000sec^-1	ASTM D3835	380 Pa·s

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	--	ISO 180	43 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ASTM D4812	530 J/m

mechanical properties	Test Condition	Test Method	Test Result
Friction coefficient	--7	ASTM D3702	0.070
	Friction coefficient	--6	ASTM D1894	0.12
		Friction coefficient	--5	ASTM D3702	0.45
		Friction coefficient	Friction coefficient	--4	ASTM D1894	0.34
shear strength		ASTM D732	84.1 Mpa
compressive strength		ASTM D695	127 Mpa
bending strength	--	ISO 178	273 Mpa
bending strength	bending strength	--	ASTM D790	265 Mpa
Bending modulus	--	ISO 178	24100 Mpa
Bending modulus	Bending modulus	--	ASTM D790	16600 Mpa
elongation	Break	ISO 527-2/1A/5	1.5 %
elongation	elongation	Break3	ASTM D638	1.5 %
Tensile modulus	--	ASTM D638	18300 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1A/1	25300 Mpa
tensile strength	Yield	ISO 527-2/1A/5	197 Mpa
tensile strength	tensile strength	--	ASTM D638	161 Mpa

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ASTME1530	0.36 W/m/K
specific heat	200°C	DSC	1670 J/kg/°C
specific heat	specific heat	50°C	DSC	1250 J/kg/°C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	1.7E-05 cm/cm/°C
Melting temperature		ASTM D3418	342 °C
Glass transition temperature		ASTM D3418	152 °C
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	299 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.18mm	ASTM D955	1.3-1.5 %
Shrinkage rate	Shrinkage rate	MD:3.18mm	ASTM D955	0.0-0.20 %
melt mass-flow rate	400°C/2.16kg	ASTM D1238	2.0 g/10min
Water absorption rate	24hr	ASTM D570	0.030 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	90

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEEK KetaSpire® PEEK KT-820SL45 SOLVAY USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet