POM M90-44 WK3068 DAICEL MALAYSIA
221
- Unit Price:US$ 3,152 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 80 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | 95.0 °C | |
| Linear coefficient of thermal expansion | 内部方法 | 1.2E-04 cm/cm/°C | |
| 内部方法 | 1.2E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | CF2001/CD3068 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.41 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10min | |
| ISO 1133 | 9.0 g/10min | ||
| Melt volume flow rate | ISO 1133 | 8.00 cm3/10min | |
| shrinkage rate | ISO 294-4 | 2.0 % | |
| ISO 294-4 | 2.0 % | ||
| Water absorption rate | ISO 62 | 0.50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| tensile strength | ISO 527-2 | 62.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| flexural modulus | ISO 178 | 2500 Mpa | |
| bending strength | ISO 178 | 87.0 Mpa | |
| coefficient of friction | JISK7218 | 0.37 | |
| JISK7218 | 0.46 | ||
| JISK7218 | 0.40 | ||
| Wear factor | JISK7218 | <1.0 10^-8mm³/N·m | |
| JISK7218 | <1.0 10^-8mm³/N·m | ||
| JISK7218 | 30 10^-8mm³/N·m | ||
| JISK7218 | 65 10^-8mm³/N·m | ||
| JISK7218 | 3500 10^-8mm³/N·m | ||
| JISK7218 | 6500 10^-8mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.