Material Description

Material Properties:High mobility｜High impact resistance｜High hardness
Application Areas:Washing machine｜Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C, Partial Break	ISO 179/1eA	50 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	55.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	50.0 J
Impact strength of cantilever beam gap	-30°C, Partial Break	ISO 180/A	45 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C, Partial Break	ISO 180/A	60 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	5800 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	4900 N

flammability	Test Condition	Test Method	Test Result
Burning rate	> 1.00 mm	ISO 3795	passed
auto-ignition temperature		ASTM D1929	530 °C
UL flame retardant rating	1.50 mm	IEC 60695-11-5	5.0 sec
UL flame retardant rating	UL flame retardant rating	2.00 mm	IEC 60695-11-5	5.0 sec
Extreme Oxygen Index		ISO 4589-2	30 %
flash temperature		ASTM D1929	450 °C
Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850 °C
Burning wire flammability index	3.0 mm	IEC 60695-2-12	900 °C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	825 °C
UL flame retardant rating	0.75 mm	UL 94	HB
Burning wire flammability index	0.75 mm	IEC 60695-2-12	850 °C
Burning wire flammability index	Burning wire flammability index	1.5 mm	IEC 60695-2-12	875 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	6.8 %
	bending strength	23°C	ISO 178	86.0 Mpa
	bending strength	bending strength	3.5% Strain, 23°C	ISO 178	68.0 Mpa
Bending modulus	23°C	ISO 178	2200 Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	> 50 %
Tensile strain	Yield, 23°C	ISO 527-2/50	5.7 %
Tensile strain	Tensile strain	Break, 23°C	ISO 527-2/50	120 %
tensile strength	Break, 23°C	ISO 527-2/50	60.0 Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2/50	58.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	2200 Mpa

injection	Test Condition	Test Method	Test Result
Exhaust hole depth			0.025 to 0.075 mm
Mold temperature			70 to 110 °C
Back pressure			10.0 to 20.0 Mpa
Processing (melt) temperature			280 to 320 °C
Temperature at the front of the material cylinder			285 to 305 °C
Spray nozzle temperature			270 to 305 °C
Temperature at the rear of the barrel			250 to 270 °C
Temperature in the middle of the barrel			270 to 290 °C
Suggested injection volume			30 to 70 %
Drying time - Dry Air Dryer			4.0 hr
Suggested maximum moisture content			< 0.020 %
Drying Temperature - Dry Air Dryer			120 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	134 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	121 °C
Vicat softening temperature	--	ISO 306/B50	141 °C
Glass transition temperature		ISO 11357-2	143 °C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	7.0E-5 cm/cm/°C
Ball Pressure Test	134°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	7.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	143 °C

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.64 g/cm³
melt mass-flow rate	300°C/1.2 kg	ISO 1133	12 g/10 min
Shrinkage rate	横向Flow	ISO 2577	0.60 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	11.0 cm3/10min
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.40 %
Shrinkage rate	Flow	ISO 2577	0.60 - 0.80 %
	Shrinkage rate	横向Flow : 280°C, 2.00 mm4	ISO 294-4	0.70 %
	Shrinkage rate	Shrinkage rate	Flow : 2.00 mm4	ISO 294-4	0.65 %
density	23°C	ISO 1183	1.19 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	23°C, 100 Hz	IEC 60250	3.20
Dielectric strength	23°C, 1.00 mm	IEC 60243-1	34 KV/mm
Volume resistivity	23°C	IEC 60093	1.0E+16 ohms·cm
Surface resistivity		IEC 60093	1.0E+16 ohms
Dissipation factor	23°C, 1 MHz	IEC 60250	0.013
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
Dissipation factor	23°C, 100 Hz	IEC 60250	1.4E-3
Relative permittivity	23°C, 1 MHz	IEC 60250	3.10

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	104 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 1837 012475 COVESTRO SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet