'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS DURAFIDE® 6165A6 HF2000 DAICEL MALAYSIA
461
- Unit Price:US$ 7,400 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:175MT
- Delivery Terms:FOB
- Port of Loading :Dongguan Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜standard｜High temperature resistance｜Filler: Glass mineral｜Filler by weight｜Filler by weight
- Application Areas:Fiber grade｜Pump parts｜Shell｜Electrical/Electronic Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 | kJ/m² |
| -30°C | ISO 179/1eU | 20 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 | kJ/m² |
| -30°C | ISO 179/1eA | 7.0 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 20 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 | |
| 0.75mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 23℃ | ISO 62 | 0.02 | % |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break | ISO 527-2/1A/5 | 130 | Mpa |
| bending strength | ISO 178 | 210 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 18800 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 | % |
| elongation | Break,23°C | ASTM D638 | 1.3 | % |
| tensile strength | Break,23°C | ASTM D638 | 114 | Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 19000 | Mpa | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 6 | kJ/m² |
| bending strength | ISO 178 | 210 | Mpa | |
| Bending modulus | ISO 178 | 18800 | Mpa | |
| elongation | Break | ISO 527-1 | 1.2 | % |
| tensile strength | ISO 527-1 | 130 | Mpa | |
| Tensile modulus | ISO 527-1 | 19000 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 2.4E-05 | cm/cm/°C |
| MD | ISO 11359-2 | 1.9E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C |
| 0.45MPa,Annealed | ASTM D648 | 280 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C |
| 1.8MPa,Unannealed | ASTM D648 | 266 | °C | |
| UL flame retardant rating | 0.750mm | UL 94 | V-0 | |
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| SpecificHeatCapacity of Melt | Internal Method | 1600 | J/kg/°C | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Shrinkage rate | MD | ISO 294-4 | 0.20-0.60 | % |
| TD | ISO 294-4 | 0.30-0.70 | % | |
| TD | ASTM D955 | 0.30-0.50 | % | |
| MD | ASTM D955 | 0.10-0.20 | % | |
| density | ISO 1183 | 1.95 | g/cm³ | |
| Specific volume | ASTM D792 | 0.502 | cm³/g | |
| density | ASTM D792 | 2.00 | g/cm³ | |
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| density | ISO 1183 | 1.95 | g/cm³ | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric constant | 1kHz | ASTM D150 | 4.50 | |
| Arc resistance | ASTM D495 | 182 | sec | |
| Dissipation factor | 1MHz | IEC 60250 | 2E-03 | |
| 1MHz | ASTM D150 | 9E-04 | ||
| 1kHz | ASTM D150 | 1E-03 | ||
| Relative permittivity | 1MHz | IEC 60250 | 5.60 | |
| Dielectric constant | 1MHz | ASTM D150 | 4.50 | |
| Dielectric strength | IEC 60243-1 | 25 | KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| ASTM D257 | 1E+16 | ohms·cm | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 100 | |
| M-Scale | ISO 2039-2 | 100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.