thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm, 注塑	ASTM D648	110 °C
melting temperature		ASTM D3418	250 °C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI		UL 746	120 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	1.0 mm	UL 94	V-0
		UL flame retardant rating	1.6 mm	UL 94	V-0 5VB
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/2.16 kg	ASTM D1238	14 g/10 min
shrinkage rate	23°C, 注塑，Flow	ASTM D955	0.60 - 1.0 %
Water absorption rate	24 hr, 23°C	ASTM D570	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity	23°C	ASTM D257	1.0E+17 ohms·cm
arc resistance		ASTM D495	PLC 7
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 0

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			245 to 255 °C
Temperature in the middle of the barrel			250 to 260 °C
Temperature at the front of the material cylinder			255 to 265 °C
Spray nozzle temperature			260 to 270 °C
Processing (melt) temperature			255 to 270 °C
mold temperature			40 to 80 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	60.8 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	> 100 %
flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	2350 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	90.2 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.