PC Makrolon®  APEC 1803 COVESTRO GERMANY

375
  • Unit Price:US$ 8,170 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    144.8MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:high viscosity｜High temperature resistance｜enhance｜Thermal stability｜Flame retardant
  • Application Areas:Automotive sector｜Laptop case｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity1000μmISO 13468-289.0 %
Refractive indexISO 4891.573
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-225 %
Burning wire flammability indexIEC 60695-2-12850 °C
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
bending strength23°CISO 178108 Mpa
Bending modulus23°CISO 1782400 Mpa
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Tensile modulus23°CISO 527-2/12400 Mpa
tensile strengthYield,23°CISO 527-2/5072.0 Mpa
Tensile strainYield,23°CISO 527-2/506.8 %
thermal performanceTest ConditionTest MethodTest Result
RTI StrUL 746150 °C
RTI ImpUL 746130 °C
RTI ElecUL 746150 °C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A159 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B174 °C
Vicat softening temperatureISO 306/B120184 °C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
density23°CISO 11831.15 g/cm³
melt mass-flow rate330°C/2.16kgISO 113310 g/10min
Melt Volume Flow Rate (MVR)330°C/2.16kgISO 113310.0 cm3/10min
Shrinkage rateTD:2.00mmISO 294-40.85 %
Shrinkage rateMD:2.00mmISO 294-40.85 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivity23°CIEC 600931E+17 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-135 KV/mm
Surface resistivityIEC 600931E+16 ohms
Dissipation factor23°C,1MHzIEC 602508E-03
Dissipation factor23°C,100HzIEC 602501E-03
Compared to the anti leakage trace indexSolutionBIEC 60112PLC 4
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 1
Relative permittivity23°C,1MHzIEC 602502.80
Relative permittivity23°C,100HzIEC 602502.90
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1121 Mpa
Supplementary InformationTest ConditionTest MethodTest Result
Electrolytic corrosion23°CIEC 60426A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.