PC LEXAN™ EXL9134 BK1A068 SABIC INNOVATIVE NANSHA

309

Unit Price:US$ 4,747 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
107.8MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High ductility at low temperature｜Short molding cycle
Application Areas:Lighting applications｜Electronic and Electrical Applications｜Aerospace Applications｜Plastic bag
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	67.0	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	825	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	825	°C
UL flame retardant rating	1.5 mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2100	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2000	Mpa
tensile strength	Yield3	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	56.0	Mpa
		tensile strength	Break3	ASTM D638	59.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	57.0	Mpa
elongation	Yield3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
	elongation	elongation	Break3	ASTM D638	120	%
bending strength	Yield, 50.0 mm Span4	ASTM D790	92.0	Mpa
bending strength	bending strength	--5,6	ISO 178	87.0	Mpa
Bending modulus	--5	ISO 178	2100	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2400	Mpa
elongation	Break	ISO 527-2/50	110	%
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			270 to 295	°C
Temperature in the middle of the barrel			280 to 305	°C
Temperature at the front of the material cylinder			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Processing (melt) temperature			295 to 315	°C
Mold temperature			70 to 95	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	120	°C
RTI Imp		UL 746	115	°C
RTI Elec		UL 746	125	°C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.2E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.2E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.1E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	141	°C
	Vicat softening temperature	--	ISO 306/B50	139	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D152510	140	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	118	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	123	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	16	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	15.0	cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.80	%
Water absorption rate	Saturation, 23°C	ISO 62	0.40	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Outdoor applicability		UL 746C	f1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.