impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	18	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	90	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	20	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	41	mm/min
UL flame retardant rating	1.5mm	UL 94	HB
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	1400	Mpa
tensile strength	Yield	ISO 527-2	41.0	Mpa
Tensile strain	Yield	ISO 527-2	30	%
Nominal tensile fracture strain		ISO 527-2	>50	%
Tensile creep modulus	1hr	ISO 899-1	1100	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	550	Mpa
Bending modulus		ISO 178	1100	Mpa
bending strength	3.5%Strain	ISO 178	34.0	Mpa
Friction coefficient	vs.Itself-Dynamic,1hr	ASTM D1894	0.32
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0	°C
Glass transition temperature		ISO 11357-2	-35.0	°C
Melting temperature		ISO 11357-3	178	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.4E-04	cm/cm/°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm
Effective thermal diffusivity coefficient			6E-08	m²/s
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	100	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
MediumDensity			1.14	g/cm³
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.90	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.35	%
density		ISO 1183	1.34	g/cm³
melt mass-flow rate		ISO 1133	2.0	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	1.70	cm3/10min
Shrinkage rate	TD	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	100Hz	IEC 60250	4.40
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.80
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	58
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	105
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	2.90	µgC/g
SpecificWear-Against		ASTM D1894	60.0	10^-6mm³/N·m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.