thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.80MPa未退火	ASTM D648	108 °C
Linear coefficient of thermal expansion	MD	ASTM D696	8.47E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTM D696	9.1E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD3.20mm	ASTM D995	0.60-0.65 %
shrinkage rate	shrinkage rate	TD3.20mm	ASTM D995	0.50-0.56 %
Water absorption rate	(23°C,24hr)	ASTM D570	0.010 %
Water absorption rate	Water absorption rate	吸湿性	ASTM D570	0.0200 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服，5mm/min，23°C	ASTM D638	46.0 Mpa
tensile strength	tensile strength	5mm/min，23°C	ASTM D638	47.0 Mpa
Elongation at break	屈服，5mm/min，23°C	ASTM D638	4.2 %
Elongation at break	Elongation at break	5mm/min，23°C	ASTM D638	100 %
Tensile modulus	50mm/min，23°C	ASTM D638	2480 Mpa
bending strength	屈服，1.3mm/min，23°C	ASTM D790	80.0 Mpa
bending strength	bending strength	1.3mm/min，23°C	ASTM D790	79.0 Mpa
flexural modulus	1.3mm/min，23°C	ASTM D790	2400 Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	600 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	悬壁梁无缺口冲击强度	ASTM D4812	NB J/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.