PPO

PPO NORYL™ PX9406-701 SABIC INNOVATIVE SHANGHAI

358

Unit Price:US$ 4,716 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
64.2MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PPO PF6049 BK KAOSO U.S.

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Household appliances｜Household appliances｜Automotive interior parts｜Electronic communication accessories｜Electronic communication accessories
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Energy at Peak	ASTM D3763	42.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1100 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.76 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 100 mm Span	ASTM D790	111 Mpa
Bending modulus	100 mm Span	ASTM D790	2640 Mpa
elongation	Break	ASTM D638	18 %
elongation	elongation	Yield	ASTM D638	9.5 %
tensile strength	Break	ASTM D638	55.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	75.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			245 to 295 °C
Temperature in the middle of the barrel			255 to 300 °C
Temperature at the front of the material cylinder			265 to 305 °C
Spray nozzle temperature			275 to 305 °C
Processing (melt) temperature			275 to 305 °C
Mold temperature			70 to 100 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm
Exhaust hole depth			0.038 to 0.051 mm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	110 °C
RTI Imp		UL 746	105 °C
RTI Elec		UL 746	110 °C
Vicat softening temperature		ASTM D15255	150 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	122 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	133 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f2
Water absorption rate	24 hr	ASTM D570	0.060 %
Shrinkage rate	Across FlowFlow 2	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	50 Hz	ASTM D150	5.2E-3
Dissipation factor	Dissipation factor	60 Hz	ASTM D150	5.2E-3
Dielectric constant	1 MHz	ASTM D150	2.49
	Dielectric constant	50 kHz	ASTM D150	2.57
	Dielectric constant	Dielectric constant	60 Hz	ASTM D150	2.57
Dielectric strength	3.20 mm, in Oil	ASTM D149	19 KV/mm
Volume resistivity		ASTM D257	2.0E+16 ohms·cm
Surface resistivity		ASTM D257	> 1.0E+16 ohms
Dissipation factor	1 MHz	ASTM D150	2.6E-3
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ PX9406-701 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet