LCP

LCP SUMIKASUPER® E6808UHF-Z SUMITOMO JAPAN

403

Unit Price:US$ 8,579 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
103.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜enhance｜Low warpage
Application Areas:--
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	350 J/m

flammability	Test Condition	Test Method	Test Result
Solder resistance		Internal Method	290 °C
Extreme Oxygen Index		ISO 527-1	48 %
UL flame retardant rating	0.30 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ASTM D790	120 Mpa
Bending modulus	23°C	ASTM D790	9400 Mpa
tensile strength		ASTM D638	100 Mpa
elongation	Break	ASTM D638	5.0 %

injection	Test Condition	Test Method	Test Result
Back pressure			1.00 to 5.00 Mpa
Mold temperature			40 to 160 °C
Maintain pressure			20.0 to 40.0 Mpa
Injection speed			中等偏快
Injection pressure			80.0 to 160 Mpa
drying time			4.0 to 24 hr
drying temperature			130 °C
Processing (melt) temperature			350 °C
Spray nozzle temperature			340 to 360 °C
Temperature at the front of the material cylinder			340 to 360 °C
Screw speed			50 to 100 rpm
Temperature at the rear of the barrel			280 to 320 °C
Temperature in the middle of the barrel			320 to 340 °C

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	6.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 150°C	Internal Method	1.0E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	240 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	Internal Method	1.0 %
Shrinkage rate	Shrinkage rate	Flow	Internal Method	0.22 %
Water absorption rate	Saturation	ASTM D570	0.020 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1 MHz	ASTM D150	0.033
Dielectric constant	1.00 GHz	ASTM D150	3.40
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.80
Volume resistivity		ASTM D257	1.0E+15 ohms·cm
Compared to the anti leakage trace index		IEC 60112	V
Arc resistance		ASTM D495	132 sec
Dissipation factor	1.00 GHz	ASTM D150	4.0E-3

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	96

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.