ABS

ABS POLYLAC® PA-717CK ZHENJIANG CHIMEI

377

Unit Price:US$ 1,912 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Thermal stability｜wear resistant｜High impact resistance｜High rigidity
Application Areas:Automotive sector｜ABS pipe｜Electrical enclosure｜Electrical appliances
Color:--
Grade:Impact resistant grade

Material Certification

MSDS

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			一般射出成型用

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	200℃ 5kg	ASTM D-1238	1.4 g/10min
melt mass-flow rate	melt mass-flow rate	200℃ 10kg	ISO 1133	14 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	1/4"	ASTM D-256	25 kg.cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/8"	ASTM D-256	28 kg.cm/cm
Rockwell hardness		ASTM D-785	115 R
tensile strength		ASTM D-638	450 kg/cm2
Bending modulus		ASTM D-790	2.5 104kg/cm2
Elongation at Break		ASTM D-790	25 %
bending strength		ASTM D-790	720 kg/cm2
Impact strength of cantilever beam gap		ASTM D256/ISO 179	27(5.2) kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	720（10.200） kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	25000（35000） kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-115
elongation		ASTM D638/ISO 527	25 %
tensile strength		ASTM D638/ISO 527	440（6.300） kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	25(4.6) kg·cm/cm(J/M)ft·lb/in

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D-1525	104(219) ℃(°F)
Hot deformation temperature	Unannealed	ASTM D-648	87(189) ℃(°F)
Hot deformation temperature	Hot deformation temperature	Annealed	ASTM D-648	98(208) ℃(°F)
Combustibility		File NO.E196075	1/16"HB
Vicat softening temperature		ASTM D1525/ISO R306	105(221) ℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	88(190) ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	99(210) ℃（℉）
Combustibility (rate)		UL 94	1/16

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238/ISO 1133	14 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	1.4 g/10min
density		ASTM D792/ISO 1183	1.05

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.