PC SABIC® 2200RGC9AT SABIC INNOVATIVE SAUDI
252
- Unit Price:US$ 1,586 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:90.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance｜High temperature resistance｜transparent｜High mobility
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 22 g/10 min | |
| Melt volume flow rate | ISO 1133 | 21.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.70 % | |
| 内部方法 | 0.50 - 0.70 % | ||
| Water absorption rate | ISO 62 | 0.35 % | |
| ASTM D570 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 120 | |
| ISO 2039-2 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 179/leA | 1.586 | |
| transmissivity | ASTM D1003 | 88.0 to 90.0 % | |
| Haze ratio | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2350 Mpa | |
| ISO 527-2/1 | 2350 Mpa | ||
| tensile strength | ASTM D638 | 63.0 Mpa | |
| ISO 527-2/50 | 63.0 Mpa | ||
| elongation | ASTM D638 | 6.0 % | |
| ISO 527-2/50 | 6.0 % | ||
| ASTM D638 | > 70 % | ||
| ISO 527-2/50 | > 70 % | ||
| Flexural modulus | ASTM D790 | 2300 Mpa | |
| ISO 178 | 2300 Mpa | ||
| bending strength | ISO 178 | 90.0 Mpa | |
| ASTM D790 | 90.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact | ASTM D3763 | 55.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 27 KV/mm | |
| dielectric constant | ASTM D150 | 3.00 | |
| ASTM D150 | 3.00 | ||
| Dissipation Factor | ASTM D150 | 1.0E-3 | |
| ASTM D150 | 0.010 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 260 to 280 °C | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the front of the material cylinder | 280 to 300 °C | ||
| Spray nozzle temperature | 270 to 290 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Temperature | 80 to 100 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 133 °C | |
| ISO 75-2/Bf | 133 °C | ||
| ASTM D648 | 122 °C | ||
| ISO 75-2/Af | 122 °C | ||
| vicat | ISO 306/B50 | 140 °C | |
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 7.0E-5 cm/cm/°C | |
| ISO 11359-2 | 7.0E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.20 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.