LCP

LCP SUMIKASUPER® E6808GHF-Z SUMITOMO JAPAN

264

Unit Price:US$ 7,144 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Low warpage｜Filler: Long glass fiber｜40% filler by weight
Application Areas:Laptop case｜Spool
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	6.40mm	ASTM D256	270 J/m

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 489	44 %
UL flame retardant rating	0.30mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
shear strength		ASTM D732	54.0 Mpa
bending strength	Yield,23°C	ASTM D790	140 Mpa
Bending modulus	23°C	ASTM D790	12500 Mpa
elongation	Break	ASTM D638	4.5 %
tensile strength	Yield	ASTM D638	130 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:150°C	Internal Method	8.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:150°C	Internal Method	4E-06 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	270 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation	ASTM D570	0.020 %
Shrinkage rate	TD	Internal Method	0.40 %
Shrinkage rate	Shrinkage rate	MD	Internal Method	0.17 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	140 sec
Dissipation factor	1.00GHz	ASTM D150	4E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.038
Dielectric constant	1.00GHz	ASTM D150	3.60
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.80
Volume resistivity		ASTM D257	1E+15 ohms·cm
Compared to the anti leakage trace index		IEC 60112	PLC 3

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	97

Supplementary Information	Test Condition	Test Method	Test Result
Solder resistance		Internal Method	280 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.