POM Delrin® 900P NC010 DUPONT NETHERLANDS
237
- Unit Price:US$ 5,280 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:67MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:lubrication｜wear resistant｜High rigidity｜high strength｜enhance｜High impact resistance｜High mobility
- Application Areas:Home appliance components｜Fiber grade｜Thin walled products
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 92 |
| R计秤 | ISO 2039-2 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 162 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 94.0 °C | |
| vicat | ISO 306/B50 | 160 °C | |
| melting temperature | ISO 11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ASTME831 | 1E-04 cm/cm/°C |
| MD | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| AnnealingTemperature | 160 °C | ||
| AnnealingTime-Optional | 30.0 min/mm | ||
| Effective thermal diffusivity coefficient | 8E-08 m²/s |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 20 mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.8mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| G-value(condensate) | ISO 6452 | 2E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 4.30 µgC/g | |
| Emission | VDA275 | <8.00 mg/kg |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| surface resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.80 |
| 1MHz | IEC 60250 | 3.80 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Hot wire ignition (HWI) | 0.750mm | UL 746 | sec |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.42 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 25 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 21.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.9 % |
| MD | ISO 294-4 | 1.9 % | |
| water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.4 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.40 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 23 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2800 Mpa |
| 1000hr | ISO 899-1 | 1500 Mpa | |
| flexural modulus | ISO 178 | 3000 Mpa | |
| coefficient of friction | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.25 |
| tensile modulus | ISO 527-2 | 3300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 71.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 12 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| 23°C | ISO 179/1eA | 8.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 200 kJ/m² |
| 23°C | ISO 179/1eU | 200 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 8.0 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.