TPEE Hytrel® DYM350 BK DUPONT USA
203
- Unit Price:US$ 5,675 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:32MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact｜Medium rigidity
- Application Areas:engineering application ｜Automotive components｜Application in the automotive field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.20 % | |
| MediumDensity | 1.00 g/cm³ | ||
| melt mass-flow rate | ISO 1133 | 15 g/10min | |
| Melt volume flow rate | ISO 1133 | 14.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 1.4 % | |
| ISO 294-4 | 1.3 % | ||
| Water absorption rate | ISO 62 | 0.60 % | |
| ISO 62 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 55 | |
| ISO 868 | 50 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | 23 mm/min | |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| FMVSS flammability | FMVSS302 | SE/B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 2.70 µgC/g | |
| Odor | VDA270 | 5.00 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 430 Mpa | |
| Tensile modulus | ISO 527-2 | 370 Mpa | |
| tensile strength | ISO 527-2 | 15.0 Mpa | |
| ISO 527-2 | 35.0 Mpa | ||
| ISO 527-2 | 10.5 Mpa | ||
| ISO 527-2 | 13.0 Mpa | ||
| ISO 527-2 | 16.0 Mpa | ||
| Tensile strain | ISO 527-2 | 43 % | |
| ISO 527-2 | >300 % | ||
| Nominal tensile fracture strain | ISO 527-2 | 600 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 39.0 J | |
| Multi axis Instrumented Peak Impact Force | ISO 6603-2 | 3200 N |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ISO 34-1 | 110 kN/m | |
| ISO 34-1 | 130 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 5E+14 ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| relative permittivity | IEC 60250 | 4.60 | |
| IEC 60250 | 4.40 | ||
| Dissipation Factor | IEC 60250 | 7E-03 | |
| IEC 60250 | 0.023 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 50.0 °C | |
| ISO 75-2/A | 40.0 °C | ||
| brittle temperature | ISO 974 | -100 °C | |
| Glass Transition Temperature | ISO 11357-2 | -55.0 °C | |
| melting temperature | ISO 11357-3 | 222 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.8E-04 cm/cm/°C | |
| ISO 11359-2 | 1.8E-04 cm/cm/°C | ||
| Effective thermal diffusivity coefficient | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.