thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	130 °C
	Heat Deflection Temperature	1.8 MPa, 未退火, 3.20 mm	ASTM D648	125 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距7	ISO 75-2/Af	127 °C
vicat		ISO 306/B120	143 °C
ball-indentation hardness	123 到 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : -40 到 40°C	ASTM E831	3.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	流动 : 23 到 80°C	ISO 11359-2	3.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	横向 : -40 到 40°C	ASTM E831	7.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.30 mm	UL 94	HB
Burning wire flammability index	2.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	850 °C

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	48 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	43 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	830 J/m
	Suspended wall beam without notch impact strength	-30°C6	ISO 180/1U	40 kJ/m²
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C6	ISO 180/1U	42 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	21.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	15 g/10 min
Melt volume flow rate	300°C/1.2 kg	ISO 1133	14.0 cm3/10min
shrinkage rate	流动 : 3.20 mm	内部方法	0.10 - 0.30 %
shrinkage rate	shrinkage rate	横向流动 : 3.20 mm	内部方法	0.10 - 0.30 %
Water absorption rate	饱和, 23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.12 %

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			265 to 290 °C
Temperature in the middle of the barrel			275 to 300 °C
Temperature at the front of the material cylinder			290 to 310 °C
Spray nozzle temperature			280 to 305 °C
Processing (melt) temperature			290 to 310 °C
mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	6400 Mpa
tensile strength	屈服3	ASTM D638	96.0 Mpa
	tensile strength	屈服	ISO 527-2/5	110 Mpa
		tensile strength	断裂3	ASTM D638	96.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/5	110 Mpa
elongation	屈服3	ASTM D638	3.0 %
	elongation	屈服	ISO 527-2/5	2.8 %
	elongation	elongation	断裂	ISO 527-2/5	2.7 %
flexural modulus	50.0 mm 跨距	ASTM D790	5850 Mpa
bending strength	屈服, 50.0 mm 跨距	ASTM D790	159 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.