PC LEXAN™  EXL4019 GY6D249 SABIC INNOVATIVE SHANGHAI

241
  • Unit Price:US$ 4,562 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    18MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Middle flow｜Short molding cycle｜Good ductility
  • Application Areas:Electronic and Electrical Applications｜Plastic bag
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376340.0 J
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA25 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span4ASTM D790103 Mpa
bending strength--5,6ISO 17898.0 Mpa
Bending modulus--5ISO 1783450 Mpa
Bending modulus50.0 mm Span4ASTM D7903500 Mpa
elongationBreakISO 527-2/58.7 %
elongationBreak3ASTM D63814 %
elongationYieldISO 527-2/54.3 %
elongationYield3ASTM D6384.3 %
tensile strengthBreakISO 527-2/548.0 Mpa
tensile strengthBreak3ASTM D63845.0 Mpa
tensile strengthYieldISO 527-2/554.0 Mpa
tensile strengthYield3ASTM D63855.0 Mpa
Tensile modulus--ISO 527-2/13900 Mpa
Tensile modulus--2ASTM D6383950 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel290 to 310 °C
Temperature in the middle of the barrel300 to 320 °C
Temperature at the front of the material cylinder310 to 330 °C
Spray nozzle temperature305 to 325 °C
Processing (melt) temperature310 to 330 °C
Mold temperature80 to 115 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648137 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Ae135 °C
Vicat softening temperatureASTM D152510146 °C
Ball Pressure Test73 to 77°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8314.7E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8317.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-27.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.40 %
Water absorption rateSaturation, 23°CISO 620.15 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.20 - 0.60 %
Shrinkage rateFlow : 3.20 mmInternal Method0.20 - 0.60 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11336.00 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D12387.5 g/10 min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.