Material Description
- Material Properties:Flame retardant｜Toughening｜UV resistance
- Application Areas:food｜Thin walled products｜Casters
- Color:--
- Grade:Special level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.18 g/cm³ | |
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| density | ISO 1183 | 1.19 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 10 g/10 min | |
| Shrinkage rate | 内部方法 | 0.40 - 0.80 % | |
| 内部方法 | 0.40 - 0.80 % | ||
| Water absorption rate | ISO 62 | 0.35 % | |
| ISO 62 | 0.15 % | ||
| Outdoor applicability | UL 746C | f1 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 90.0 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 825 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 35 % | |
| UL flame retardant rating | UL 94 | 5VA | |
| UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 52.0 J | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Impact strength of cantilever beam gap | ISO 180/4A | 80 kJ/m² | |
| ISO 180/1A | 70 kJ/m² | ||
| ISO 180/1A | 55 kJ/m² | ||
| ISO 180/4A | 65 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 75 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 800 J/m | |
| 内部方法 | 1100 J/m | ||
| ASTM D256 | 640 J/m | ||
| ASTM D256 | 590 J/m | ||
| ASTM D256 | 680 J/m | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D790 | 88.0 Mpa | |
| ISO 178 | 85.0 Mpa | ||
| Flexural modulus | ISO 178 | 2200 Mpa | |
| ASTM D790 | 2060 Mpa | ||
| elongation | ISO 527-2/50 | 130 % | |
| ASTM D638 | 130 % | ||
| ISO 527-2/50 | 6.0 % | ||
| tensile strength | ISO 527-2/50 | 55.0 Mpa | |
| ASTM D638 | 61.0 Mpa | ||
| ISO 527-2/50 | 60.0 Mpa | ||
| elongation | ASTM D638 | 6.0 % | |
| tensile strength | ASTM D638 | 58.0 Mpa | |
| Tensile modulus | ISO 527-2/1 | 2100 Mpa | |
| ASTM D638 | 2100 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| screw speed | 40 to 70 rpm | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Temperature at the rear of the barrel | 215 to 295 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| Suggested maximum moisture content | 0.020 % | ||
| drying time | 3.0 to 4.0 hr | ||
| drying temperature | 120 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| IEC 60112 | V | ||
| Dissipation Factor | IEC 60250 | 1.0E-3 | |
| IEC 60250 | 1.0E-3 | ||
| ASTM D150 | 8.5E-3 | ||
| ASTM D150 | 2.4E-3 | ||
| ASTM D150 | 2.4E-3 | ||
| dielectric constant | IEC 60250 | 2.60 | |
| IEC 60250 | 2.70 | ||
| IEC 60250 | 2.60 | ||
| ASTM D150 | 2.90 | ||
| ASTM D150 | 2.95 | ||
| dielectric strength | IEC 60243-1 | 16 KV/mm | |
| dielectric constant | ASTM D150 | 2.95 | |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI Elec | UL 746 | 125 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 7.7E-5 cm/cm/°C | |
| ASTM E831 | 6.7E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.2E-5 cm/cm/°C | ||
| ASTM E831 | 6.7E-5 cm/cm/°C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| vicat | ISO 306/B50 | 140 °C | |
| ASTM D152512 | 142 °C | ||
| Heat distortion temperature | ASTM D648 | 124 °C | |
| ISO 75-2/Ae | 124 °C | ||
| ASTM D648 | 120 °C | ||
| ISO 75-2/Be | 135 °C | ||
| ASTM D648 | 134 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.