PC Makrolon® 1837 COVESTRO GERMANY
207
- Unit Price:US$ 6,874 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜High temperature resistance
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 104 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Linear coefficient of thermal expansion | 横向 : 23 到 55°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 流动 : 23 到 55°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| ball-indentation hardness | 134°C | IEC 60695-10-2 | 通过 |
| vicat | -- | ISO 306/B120 | 143 °C |
| -- | ISO 306/B50 | 141 °C | |
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 121 °C |
| Glass Transition Temperature | ISO 11357-2 | 143 °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 134 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | > 1.00 mm | ISO 3795 | passed |
| auto-ignition temperature | ASTM D1929 | 530 °C | |
| UL flame retardant rating | 2.00 mm | IEC 60695-11-5 | 5.0 sec |
| 1.50 mm | IEC 60695-11-5 | 5.0 sec | |
| flash temperature | ASTM D1929 | 450 °C | |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % | |
| Hot filament ignition temperature | 2.0 mm | IEC 60695-2-13 | 825 °C |
| 1.5 mm | IEC 60695-2-13 | 825 °C | |
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 875 °C |
| 3.0 mm | IEC 60695-2-12 | 900 °C | |
| 0.75 mm | IEC 60695-2-12 | 850 °C | |
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 5800 N |
| 23°C | ISO 6603-2 | 4900 N | |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 50.0 J |
| Impact strength of cantilever beam gap | 23°C, 局部断裂 | ISO 180/A | 60 kJ/m² |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 55.0 J |
| Impact strength of cantilever beam gap | -30°C, 局部断裂 | ISO 180/A | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | 23°C, 局部断裂 | ISO 179/1eA | 60 kJ/m² |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C, 局部断裂 | ISO 179/1eA | 50 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 °C | ||
| Drying time - Dry Air Dryer | 4.0 hr | ||
| Exhaust hole depth | 0.025 to 0.075 mm | ||
| mold temperature | 70 to 110 °C | ||
| Back pressure | 10.0 to 20.0 Mpa | ||
| Processing (melt) temperature | 280 to 320 °C | ||
| Spray nozzle temperature | 270 to 305 °C | ||
| Temperature at the front of the material cylinder | 285 to 305 °C | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| Suggested maximum moisture content | < 0.020 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 B | IEC 60112 | PLC 4 |
| 解决方案 A | IEC 60112 | PLC 3 | |
| Dissipation Factor | 23°C, 100 Hz | IEC 60250 | 1.4E-3 |
| 23°C, 1 MHz | IEC 60250 | 0.013 | |
| relative permittivity | 23°C, 1 MHz | IEC 60250 | 3.10 |
| dielectric strength | 23°C, 1.00 mm | IEC 60243-1 | 34 KV/mm |
| relative permittivity | 23°C, 100 Hz | IEC 60250 | 3.20 |
| volume resistivity | 23°C | IEC 60093 | 1.0E+16 ohms·cm |
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| shrinkage rate | 流量 : 2.00 mm4 | ISO 294-4 | 0.65 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.40 % |
| shrinkage rate | 横向流量 : 280°C, 2.00 mm4 | ISO 294-4 | 0.70 % |
| 流量 | ISO 2577 | 0.60 - 0.80 % | |
| 横向流量 | ISO 2577 | 0.60 - 0.80 % | |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 11.0 cm3/10min |
| Apparent density | ISO 60 | 0.64 g/cm³ | |
| melt mass-flow rate | 300°C/1.2 kg | ISO 1133 | 12 g/10 min |
| density | 23°C | ISO 1183 | 1.19 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 3.5% 应变, 23°C | ISO 178 | 68.0 Mpa |
| 23°C | ISO 178 | 6.8 % | |
| 23°C | ISO 178 | 86.0 Mpa | |
| flexural modulus | 23°C | ISO 178 | 2200 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2/50 | 120 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 % |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 5.7 % |
| tensile strength | 断裂, 23°C | ISO 527-2/50 | 60.0 Mpa |
| 屈服, 23°C | ISO 527-2/50 | 58.0 Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.