PC LEXAN™ 915R-8T8D133 SABIC INNOVATIVE US
63
- Unit Price:US$ 3,275 /MT
- Packaging Specification:
- Supply Quantity:15MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Easy to demould
- Application Areas:Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 132 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 123 °C | |
| vicat | ASTM D15255 | 138 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| 1.1mm | UL 94 | V-0 | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| 1.6mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 800 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 67.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2400 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 63.0 Mpa |
| 断裂 | ASTM D638 | 62.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| 断裂 | ASTM D638 | 130 % | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2460 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 93.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.