PA66

PA66 Vydyne® R533H BAT ASCEND USA

186

Unit Price:US$ 3,211 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
37MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Burning wire flammability index	0.75mm	IEC 60695-2-12	725 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	700 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	875 °C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	750 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	10600 Mpa
tensile strength	Break,23°C	ISO 527-2	205 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
Bending modulus	23°C	ISO 178	10200 Mpa
bending strength	23°C	ISO 178	290 Mpa
Poisson's ratio		ISO 527-2	0.40

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	1.5mm	UL 746	140 °C
RTI Elec	RTI Elec	3.0mm	UL 746	140 °C
RTI Imp	0.75mm	UL 746	125 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Melting temperature		ISO 11357-3	260 °C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	2.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
RTI Elec	0.75mm	UL 746	140 °C
RTI Imp	1.5mm	UL 746	125 °C
RTI Imp	RTI Imp	3.0mm	UL 746	125 °C
RTI Str	0.75mm	UL 746	140 °C
	RTI Str	1.5mm	UL 746	140 °C
	RTI Str	RTI Str	3.0mm	UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.80 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.7 %
Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.40 %

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	1.5mm	UL 746	PLC 0
High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Hot wire ignition	0.75mm	UL 746	PLC 4
	Hot wire ignition	1.5mm	UL 746	PLC 3
	Hot wire ignition	Hot wire ignition	3.0mm	UL 746	PLC 4
Volume resistivity	0.750mm	IEC 60093	1E+13 ohms·cm
Dielectric strength	1.00mm	IEC 60243	20 KV/mm
Arc resistance	3.00mm	ASTM D495	PLC6
Compared to the anti leakage trace index	3.00mm	IEC 60112	V
High arc combustion index	0.75mm	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Vydyne® R533H BAT ASCEND USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet