ABS POLYLAC® PA-716 TAIWAN CHIMEI

443

Unit Price:US$ 2,570 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
Kaoshiung port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:Home appliance components
Color:--
Grade:High liquidity level

Material Certification

MSDS

RoHS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	25	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	210	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	240	J/m
Charpy Notched Impact Strength	23°C	ISO 179	26	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-2/50	25	%
elongation	elongation	Break4	ASTM D638	25	%
tensile strength	Break	ISO 527-2/50	31.0	Mpa
	tensile strength	Yield	ISO 527-2/50	42.0	Mpa
	tensile strength	tensile strength	Yield4	ASTM D638	43.6	Mpa
bending strength	--6	ISO 178	65.0	Mpa
Bending modulus	--5	ASTM D790	2340	Mpa
Bending modulus	Bending modulus	--6	ISO 178	1900	Mpa
bending strength	--5	ASTM D790	68.4	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	95.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	83.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9.1E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	96.0	°C
	Vicat softening temperature	--	ISO 306/A50	104	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15257	105	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	97.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	--3	ASTM D792	1.04	g/cm³
density	density	23°C	ISO 1183	1.04	g/cm³
Shrinkage rate		ISO 294-4	0.40-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	33.0	cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	3.5	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

ABS POLYLAC® PA-716 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index