Material Properties:High temperature resistance｜Flame retardant｜Filler: Glass fiber reinforced material
Application Areas:Electronic and electrical accessories｜Automotive components｜Casters
Color:--
Grade:Light diffusion level

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
1.8MPa, Unanealed, 3.20mm		ASTM D648	138 °C
1.8MPa, Unanealed, 64.0mm span		ISO 75-2/Af	140 °C
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	2.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	6.9E-05 cm/cm/°C

Impact resistance	Test Condition	Test Method	Test Result
23°C		ISO 180/1A	19 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	28.2 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	19 kJ/m²
23°C		ASTM D256	240 J/m

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ASTM D1238	4.5 g/10min
Melt volume flow rate	300°C/1.2kg	ISO 1133	5.00 cm3/10min
shrinkage rate	MD：3.20mm	内部方法	0.20-0.60 %
Water absorption rate	饱和,23°C	ISO 62	0.20 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.30 %

mechanical properties	Test Condition	Test Method	Test Result
fracture		ISO 527-2/5	57.0 Mpa
yield		ISO 527-2/5	0.30 %
fracture		ASTM D638	5.0 %
fracture	fracture		ISO 527-2/5	1.8 %
50.0mm span		ASTM D790	4860 Mpa
--5		ISO 178	5480 Mpa
--6		ISO 178	100 Mpa
Yield, 50.0mm span		ASTM D790	99.0 Mpa
--1		ASTM D638	5200 Mpa
yield		ISO 527-2/5	11.0 Mpa
fracture		ASTM D638	52.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.