PPO

PPO FLEX NORYL™ WCD931 BK1066 SABIC INNOVATIVE US

199

Unit Price:US$ 424 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
11.2MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜transparent
Application Areas:Automotive interior parts
Color:--
Grade:Extrusion grade

Technical Data Sheet

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreA,30Sec	ASTM D2240	93

thermal performance	Test Condition	Test Method	Test Result
Brittle temperature		ASTM D746	<-40.0 °C
Hot deformation temperature	100°C	CCP METHOD	10 %

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	3.0mm	IEC 60695-2-12	750 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775 °C
Extreme Oxygen Index		ISO 4589-2	29 %
Smoke density	Flame,0.5mmplaque,Ds,max	ASTME662	56
Smoke density	Smoke density	Non-Flame,0.5mmplaque,Ds,max	ASTME662	150
VerticalFlameTest		EN50265-2-1	PASSES

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	2E+15 ohms·cm
Dielectric strength	2.00mm,inOil	IEC 60243-1	23 KV/mm
Dielectric constant	1MHz	ASTM D150	3.00
Dissipation factor	1MHz	ASTM D150	1E-03
Compared to the anti leakage trace index		IEC 60112	V

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/10.0kg	ASTM D1238	8.5 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	100mmSpan	ASTM D790	160 Mpa
Bending modulus	Bending modulus		ISO 178	135 Mpa
tensile strength	Break	CCP METHOD	15.0 Mpa
	tensile strength	Break2	ASTM D638	9.00 Mpa
		tensile strength	Break,80°C3	CCP METHOD	15.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	9.00 Mpa
elongation	Break	CCP METHOD	310 %
	elongation	Break2	ASTM D638	130 %
	elongation	elongation	Break,80°C3	CCP METHOD	270 %
Tensile strain	Break	ISO 527-2/50	180 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO FLEX NORYL™ WCD931 BK1066 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet