PC Makrolon®  RX1805 451118 COVESTRO GERMANY

372
  • Unit Price:US$ 7,291 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    58MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:transparent
  • Application Areas:Medical Supplies
  • Color:--
  • Grade:Special level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Multi axis Instrumented Peak Impact Force23°CISO 6603-25700 N
Multi axis Instrumented Peak Impact Force-30°CISO 6603-26600 N
Multi axis Instrumented Impact Energy23°CISO 6603-265.0 J
Multi axis Instrumented Impact Energy-30°CISO 6603-270.0 J
Impact strength of cantilever beam gap23°C,Partial BreakISO 739170 kJ/m²
Charpy Notched Impact Strength-30°C,Complete BreakISO 739116 kJ/m²
Charpy Notched Impact Strength23°C,Partial BreakISO 739180 kJ/m²
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739115 kJ/m²
flammabilityTest ConditionTest MethodTest Result
SelfIgnitionASTM D1929550 °C
FlashIgnitionTemperatureASTM D1929480 °C
Extreme Oxygen IndexISO 4589-227 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/12400 Mpa
tensile strengthYield,23°CISO 527-2/5067.0 Mpa
tensile strengthBreak,23°CISO 527-2/5075.0 Mpa
Tensile strainYield,23°CISO 527-2/506.3 %
Tensile strainBreak,23°CISO 527-2/50130 %
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Bending modulus23°CISO 1782400 Mpa
bending strength3.5%Strain,23°CISO 17873.0 Mpa
bending strength23°CISO 17898.0 Mpa
Bending strain23°CISO 1787.1 %
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/B50144 °C
Glass transition temperatureISO 11357-2145 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A126 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B138 °C
thermal conductivity23°CISO 83020.20 W/m/K
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Ball Pressure Test135°CIEC 60695-10-2Pass
Vicat softening temperature--ISO 306/B120145 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateTD:2.00mm3ISO 294-40.70 %
Shrinkage rateMD:2.00mm3ISO 294-40.70 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
density23°CISO 11831.20 g/cm³
Shrinkage rateMDISO 25770.60-0.80 %
Shrinkage rateTDISO 25770.60-0.80 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11336.00 cm3/10min
melt mass-flow rate300°C/1.2kgISO 11336.5 g/10min
Apparent densityISO 600.66 g/cm³
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1114 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.