PA66 Durethan®  AKV35H2.0 901510 LANXESS GERMANY

353
  • Unit Price:US$ 4,960 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:Table products｜Washer｜Toy
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U75 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U65 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU85 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU75 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.6mmUL 94HB
UL flame retardant rating3.2mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12650 °C
Extreme Oxygen IndexISO 4589-226 %
BurningBehavior>1.00mmISO 3795passed
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-2/111500 Mpa
Tensile modulus23°CASTM D63811000 Mpa
bending strengthFlexuralStrainatFlexuralStrength6(23°C)3.8 %
bending strength23°CISO 178305 Mpa
bending strength3.5%StrainISO 178/A-- Mpa
bending strength23°CASTM D790290 Mpa
Bending modulus23°CISO 178/A10700 Mpa
Bending modulus23°CASTM D79010000 Mpa
Tensile strainBreak,23°CISO 527-2/53.1 %
elongationBreak,23°CASTM D6383.0 %
tensile strengthBreak,23°CISO 527-2/5195 Mpa
tensile strengthBreak,23°CASTM D638190 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,4.00mmASTM D648>249 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B250 °C
Hot deformation temperature0.45MPa,Unannealed,4.00mmASTM D648>249 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A245 °C
Vicat softening temperature--ISO 306/B50>230 °C
Vicat softening temperature--ISO 306/B120255 °C
Melting temperatureISO 11357-3262 °C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-22E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-28E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 621.7 %
Water absorption rateSaturation,23°CISO 625.2 %
Shrinkage rateMD:120°C,2hr,2.00mm3ISO 294-40.060 %
Shrinkage rateMD:300°C,2.00mm2ISO 294-40.38 %
Shrinkage rateTD:120°C,2hr,2.00mm3ISO 294-40.090 %
Shrinkage rateTD:300°C,2.00mm2ISO 294-41.1 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600931E+14 ohms
Volume resistivity23°CIEC 600931E+15 ohms·cm
Dielectric strength23°C,1.00mmIEC 60243-135 KV/mm
Dielectric strength23°C,3.00mmIEC 60243-140 KV/mm
Dielectric constant23°C,50HzIEC 602504.00
Dielectric constant23°C,1MHzIEC 602504.00
Relative permittivity23°C,100HzIEC 602503.90
Relative permittivity23°C,1MHzIEC 602503.60
Dissipation factor23°C,50HzIEC 602506E-03
Dissipation factor23°C,100HzIEC 602500.010
Dissipation factor23°C,1MHzIEC 602504.0E-30.015
Compared to the anti leakage trace indexSolutionAIEC 60112 V
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA66.GHRW.14-110.GF30
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.