TPEE RITEFLEX® 663 CELANESE USA
181
- Unit Price:US$ 3,329 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance
- Application Areas:Automotive components｜High temperature hot plugging adhesive
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 63 |
| 邵氏D,15秒 | ISO 868 | 63 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 114 °C |
| Glass Transition Temperature | ASTM D3418 | -42.8 °C | |
| vicat | ASTM D1525 | 195 °C | |
| melting temperature | ASTM D3418 | 210 °C | |
| ISO 11357-3 | 212 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | Kg/m | 269.7 kN/m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ASTM D624 | 266 kN/m | |
| 流动方向 | ISO 34-1 | 160 kN/m | |
| compression set | 23°C | ASTM D395 | <1.0 % |
| Shore hardness | -- | 内部方法 | 40 % |
| -- | ASTM D2632 | 40 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.820 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 16 g/10min | |
| 240°C/2.16kg | ISO 1133 | 19 g/10min | |
| shrinkage rate | MD | ASTM D955 | 1.9 % |
| TD | ISO 294-4 | 1.7-2.1 % | |
| MD | ISO 294-4 | 1.7-2.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| volume resistivity | ASTM D257 | 2E+13 ohms·cm | |
| IEC 60093 | 2E+15 ohms·cm | ||
| dielectric strength | ASTM D149 | 13 KV/mm | |
| IEC 60243-1 | 14 KV/mm | ||
| relative permittivity | 1MHz | IEC 60250 | 4.00 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.040 |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | V | |
| IEC 60112 | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 365 Mpa |
| ISO 527-2/1A/1 | 350 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/1A/50 | 22.0 Mpa |
| 断裂,23°C | ASTM D638 | 26.2 Mpa | |
| 断裂 | ISO 527-2/1A/50 | 38.0 Mpa | |
| 5.0%应变 | ISO 527-2 | 13.0 Mpa | |
| 10%应变 | ISO 527-2 | 18.0 Mpa | |
| 50%应变 | ISO 527-2/1A/50 | 21.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 44 % |
| elongation | 断裂,23°C | ASTM D638 | 320 % |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | >50 % | |
| flexural modulus | -40°C | ISO 178 | 1900 Mpa |
| 23°C | ISO 178 | 325 Mpa | |
| bending strength | 23°C | ISO 178 | 17.5 Mpa |
| RossFlex | 内部方法 | >1.0E+6 cycles |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.