thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm	ASTM D648	> 250 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	> 250 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	3.20 mm，Flow	ASTM D955	0.10 - 0.20 %

injection	Test Condition	Test Method	Test Result
drying temperature			100 to 120 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			300 °C
Temperature in the middle of the barrel			310 °C
Temperature at the front of the material cylinder			320 °C
Spray nozzle temperature			330 °C
Processing (melt) temperature			300 to 330 °C
mold temperature			120 to 150 °C
screw speed			< 100 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	断裂, 3.20 mm	ASTM D638	180 Mpa
elongation	断裂, 3.20 mm	ASTM D638	1.0 to 2.0 %
flexural modulus	3.20 mm	ASTM D790	13500 Mpa
bending strength	3.20 mm	ASTM D790	255 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.