ABS

ABS POLYLAC® PA-764 TAIWAN CHIMEI

284

Unit Price:US$ 6,046 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS AF-303G LG CHEM KOREA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Weather resistance｜heat-resisting
Application Areas:Home appliance components｜Fitness equipment｜Electronic field｜Electrical field
Color:--
Grade:Weather resistant grade

Material Certification

MSDS

RoHS

Technical Data Sheet

other	Test Condition	Test Method	Test Result
remarks			在射出周期中勿将热融胶长期停留在加热管中
characteristic			难燃性耐光性耐热性
Color			-
purpose			计算机配件 / 电子产品零配件 / 电动工具零配件 / 电视机外壳 / 事务机器等

machinability	Test Condition	Test Method	Test Result
Dry conditions			80°C下烘料约2-3小时
Processing temperature			180-220 °C
	Processing temperature			190-220 °C
	Processing temperature	Processing temperature			180-220°C °C
pressure			50-60kg/cm² Mpa
	pressure			5-10kg/cm² Mpa
	pressure	pressure			20-50kg/cm² Mpa
Melt Temperature			- °C
Mold temperature			40-70°C °C
Screw speed			- rpm

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	12(2.2) kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	- %
Tensile modulus		ASTM D638/ISO 527	- kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	370（5.250） kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	15 %
Rockwell hardness		ASTM D785	R-98
Bending modulus		ASTM D790/ISO 178	20000(28000) kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	590（8.360） kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	14（2.6） kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	- %

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	1.6mm.V-0 2.5mm.5VA
Hot deformation temperature	HDT	ASTM D648/ISO 75	92（198） ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	78（174） ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	97（207） ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	- mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.19
Shrinkage rate		ASTM D955	- %
Water absorption rate		ASTM D570/ISO 62	- %
melt mass-flow rate		ASTM D1238/ISO 1133	3.2 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	32 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.